- Substrate : Crystal Quartz
- Surface Figure : λ/10 @ 633nm
- Surface Quality : 10-5 Laser Quality
- Diameters : 5.0mm to 2.0inch
- Diameter Tolerance : +0.0/-0.20mm
- Parallelism : ≤ 1.0 arc min.
- AR Coating : R < 0.25%
- Wavelengths : 213 to 2020nm
- Retardation : λ/2 or λ/4
- Retardation Tolerance : λ500 at 20 Å˚ C
- Damage Threshold : > 10 mJ/㎠ 10 nsec pulse
- Clear Aperture : > 85% of diameter
Waveplate
ZERO ORDER QUARTZ WAVEPLATE
MULTIPLE ORDER QUARTZ WAVEPLATE
- Substrate : Crystal Quartz
- Surface Figure : λ/10 @ 633nm
- Surface Quality : 10-5 Laser Quality
- Diameters : 5.0mm to 2.0inch
- Diameter Tolerance : +0.0/-0.20mm
- Parallelism : ≤ 1.0 arc min.
- AR Coating : R < 0.25%
- Wavelengths : 213 to 2020nm
- Retardation : λ/2 or λ/4
- Retardation Tolerance : λ/500 at 20 Å˚ C
- Damage Threshold : > 10 mJ/㎠ 10 nsec pulse
- Clear Aperture : > 85% of diameter
POLARIZATION ROTATORS
- Substrate : Crystal Quartz
- Transmitted Wavefront : λ/4 @ 633nm
- Surface Quality : 20-10 Laser Quality
- Diameter Tolerance : +0.0/-0.25mm
- Damage Threshold : > 100 mJ/㎠ 10 nsec pulse
- Beam Deviation : ≤ 3 arc min.
- Clear Aperture : > 90% of diameter
- Adhesion and Durability : Per MIL-C-675A
DUAL WAVELENGTH WAVEPLATE
- Substrate : Crystal Quartz
- Surface Figure : λ/10 @ 633nm
- Surface Quality : 10-5 Laser Quality
- Diameters : 5.0mm to 2.0 inch
- Diameter Tolerance : +0.0/-0.20mm
- Parallelism : ≤ 1.0 arc min.
- AR Coating : R < 0.5%
- Retardation : λ/100 at 20 Å˚ C
- Damage Threshold : > 2 J/㎠ 10 nsec pulse
- Clear Aperture : > 90% of diameter
- Adhesion and Durability : Per MIL-C-675A
OPTICAL BEAM ISOLATORS
- Substrate : BK7 or Crystal Quartz
- Transmitted Wavefront : λ/4 @ 633nm
- Surface Quality : 20-10 Laser Quality
- Diameter Tolerance : +0.0/-0.25mm
- Damage Threshold : > 100 mJ/㎠ 10 nsec pulse
- Beam Deviation : ≤ 3 arc min.
- Reflectance Efficiency : Rs > 99.0%
- Clear Aperture : > 90% of diameter
- Adhesion and Durability : Per MIL-C-675A